Title : ( Investigating the Effect of Mechanical Activation Parameters on Structural Changes and Leaching Rate of Molybdenite Concentrate )

Authors: Hossein Shalchian , Jalil Vahdati Khaki , Abolfazl Babakhani , M. Torabi Parizi ,

Access to full-text not allowed by authors

Citation: BibTeX | EndNote

Abstract

In this research, mechanical activation (MA) was employed for leaching rate improvement of molybdenite concentrate in nitric acid media. These experiments were performed in two groups: with and without aluminum oxide (alumina). A full factorial design was used for each group of experiments. Leaching rate increment up to 5 times was observed only in 2 hours activation procedure. XRD analysis demonstrated structural disordering in activated MoS2. TEM images showed that particle size has been reduced to nanoscale. The initial powder size was 80% between 2-44 µm and dropped to about 10nm and 140nm in MA experiments with and without alumina, respectively. This size reduction would be the main reason of leaching rate enhancement which is more achievable in MA in presence of alumina. The results demonstrate that alumina has a motivating effect in activation procedure to achieve a nanostructure molybdenite. Analysis of variance revealed milling speed is the main parameter in MA without alumina, while, ball to powder ratio is the most important factor in MA procedure in presence of alumina on leaching rate.

Keywords

Mechanical activation; Leaching rate; Nanostructure molybdenite; Analysis of variance .
برای دانلود از شناسه و رمز عبور پرتال پویا استفاده کنید.

@inproceedings{paperid:1066232,
author = {Shalchian, Hossein and Vahdati Khaki, Jalil and Babakhani, Abolfazl and M. Torabi Parizi},
title = {Investigating the Effect of Mechanical Activation Parameters on Structural Changes and Leaching Rate of Molybdenite Concentrate},
booktitle = {5th International Biennial Conference on Ultrafine Grained and Nanostructured Materials, UFGNSM15},
year = {2015},
location = {تهران, IRAN},
keywords = {Mechanical activation; Leaching rate; Nanostructure molybdenite; Analysis of variance .},
}

[Download]

%0 Conference Proceedings
%T Investigating the Effect of Mechanical Activation Parameters on Structural Changes and Leaching Rate of Molybdenite Concentrate
%A Shalchian, Hossein
%A Vahdati Khaki, Jalil
%A Babakhani, Abolfazl
%A M. Torabi Parizi
%J 5th International Biennial Conference on Ultrafine Grained and Nanostructured Materials, UFGNSM15
%D 2015

[Download]