Title : ( A novel process on production of thin wall austempered ductile iron heat-treted in the mold )

Authors: Ali Reza Kiani Rashid , Abolfazl Babakhani , ,

Citation: BibTeX | EndNote

Abstract

In this study, the production of thin wall austempered ductile iron, heat treated in the mold and in the presence of Ni and Mo was investigated. The base iron was melted in an induction furnace and treated at 1450°C by plunging and sandwich methods. Ductile irons were cast in two molds: one was a strip metallic mold with the thickness of 3mm and another cylindrical mold with diameter of 2.5cm. After casting, the specimens were austempered at 350°C for 1hr. Then the microstructures of the specimens were examined by optical microscopy. Results indicated that the ausferrite microstructure can be achieved by the control of the cooling rate within temperature range between 280-400°C. Austempering time about Ihr resulted in no trace of martensite and the structure was only composed of bainitic-ferrite and high carbon retained austenite.

Keywords

Bainite; Casting; Heat treatment; Phase transformation
برای دانلود از شناسه و رمز عبور پرتال پویا استفاده کنید.

@inproceedings{paperid:1025087,
author = {Kiani Rashid, Ali Reza and Babakhani, Abolfazl and , },
title = {A novel process on production of thin wall austempered ductile iron heat-treted in the mold},
booktitle = {TMS 2010 - 139th Annual Meeting and Exhibition},
year = {2010},
location = {Seattle, WA, USA},
keywords = {Bainite; Casting; Heat treatment; Phase transformation},
}

[Download]

%0 Conference Proceedings
%T A novel process on production of thin wall austempered ductile iron heat-treted in the mold
%A Kiani Rashid, Ali Reza
%A Babakhani, Abolfazl
%A ,
%J TMS 2010 - 139th Annual Meeting and Exhibition
%D 2010

[Download]