In this research, Ce0.8Zr0.2-xMnxO2 nano particles (x = 0.0, 0.05, 0.10) were synthesized at 600 Co-calcination temperature by co-precipitation method. The starting materials were cerium and zirconium nitrates, manganese chloride and ammonia as a precipitating agent. The crystalline structure of the synthesized samples was studied by X-ray diffraction (XRD) technique. TEM images of the prepared Ce0.8Zr0.2O2and Ce0.8Zr0.1Mn0.1O2 showed that their average particle size are about 8.2 and 7.3 nm, respectively. Fourier transform infrared (FTIR) spectroscopy was used to investigate the present bonds in the synthesized samples.
کلمات کلیدی
, co, precipitation; ceria, zirconia; manganese; XRD; TEM; FTIR@article{paperid:1063946,
author = {نورالدینی, رضا and کمپانی, احمد and قربانی, شعبان رضا},
title = {بررسی خواص ساختاری نانو ذرات سریا- زیرکونیا آلاییده با منگنز سنتز شده به روش هم رسوبی},
journal = {Iranian Journal crystallography and mineralogy- بلور شناسی و کانی شناسی ایران},
year = {2017},
volume = {25},
number = {2},
month = {July},
issn = {1561-6290},
pages = {455--460},
numpages = {5},
keywords = {co-precipitation; ceria-zirconia; manganese; XRD; TEM; FTIR},
}
%0 Journal Article
%T بررسی خواص ساختاری نانو ذرات سریا- زیرکونیا آلاییده با منگنز سنتز شده به روش هم رسوبی
%A نورالدینی, رضا
%A کمپانی, احمد
%A قربانی, شعبان رضا
%J Iranian Journal crystallography and mineralogy- بلور شناسی و کانی شناسی ایران
%@ 1561-6290
%D 2017