بیستمین همایش بلورشناسی و کانی شناسی ایران , 2013-01-30

عنوان : ( بررسی ویژگیهای ساختاری، میکروسکوپی و مغناطیسی ترکیب MmNi۴/۲۲Co۰/۴۸Mn۰/۱۵Al۰/15 )

نویسندگان: سید مجتبی زارعی , هادی عربی , فائز پورآرین ,
فایل: Full Text

استناددهی: BibTeX | EndNote

چکیده

The MmNi4.22Co0.48Mn0.15Al0.15 (Mm = mixed rare earth metals) compound was synthesized by a vacuum induction melting system under argon atmosphere. The sample was characterized by X-ray diffraction and the scanning electron microscopy with energy dispersive X-ray detector. The structural results show that the sample is single phase with CaCu5 type hexagonal structure, and there is no secondary phase. However, the substitutions at La and Ni site cause the lattice expansion. The Study of surface morphology by scanning electron microscope (SEM) equipped with energy dispersive X-ray (EDX) confirms the homogeneous composition and the existence of any precipitated solid solution phases, in agreement with XRD results. The magnetic measurements result reveals a weak magnetic property at room temperature.

کلمات کلیدی

, MmNi4.22Co0.48Mn0.15Al0.15, induction melting, structural, surface morphology, magnetic propertied
برای دانلود از شناسه و رمز عبور پرتال پویا استفاده کنید.

@inproceedings{paperid:1033988,
author = {سید مجتبی زارعی and عربی, هادی and فائز پورآرین},
title = {بررسی ویژگیهای ساختاری، میکروسکوپی و مغناطیسی ترکیب MmNi۴/۲۲Co۰/۴۸Mn۰/۱۵Al۰/15},
booktitle = {بیستمین همایش بلورشناسی و کانی شناسی ایران},
year = {2013},
location = {اهواز, ايران},
keywords = {MmNi4.22Co0.48Mn0.15Al0.15; induction melting; structural; surface morphology; magnetic propertied},
}

[Download]

%0 Conference Proceedings
%T بررسی ویژگیهای ساختاری، میکروسکوپی و مغناطیسی ترکیب MmNi۴/۲۲Co۰/۴۸Mn۰/۱۵Al۰/15
%A سید مجتبی زارعی
%A عربی, هادی
%A فائز پورآرین
%J بیستمین همایش بلورشناسی و کانی شناسی ایران
%D 2013

[Download]