عنوان : ( ساخت و مشخصه یابی ساختاری، میکروسکوپی و مغناطیسی آلیاژ سه تایی 2 Zr0.5Ti0.5Cr )
نویسندگان: رضا سرحدی , هادی عربی , فائز پورآرین ,
دانلود فایل برای اعضای دانشگاهبر اساس تصمیم نویسنده مقاله دسترسی به متن کامل برای اعضای غیر دانشگاه ممکن نیست
چکیده
In this paper, the report on preparation and physical characterization of Zr0.5Ti0.5Cr2 alloy are presented. This alloy was prepared by induction melting method. The XRD results show that this alloy is single phase with hexagonal structure (C14-type Laves phase-P63/mmc space group). Any trace of other phases such as C15 and C36 were not observed. Optical and scanning electron microscope pictures obtained from the surface of alloy indicate the formation of dendrite structure consist of light and dark regions on surface of alloy. The EDX analysis shows different atomic percentage in these regions. Properties measurements present paramagneticlike behavior for this alloy.
کلمات کلیدی
, Zr0.5Ti0.5Cr2 alloy, induction melting method, C14-type Laves phase
@inproceedings{paperid:1033994,
author = {رضا سرحدی and عربی, هادی and فائز پورآرین},
title = {ساخت و مشخصه یابی ساختاری، میکروسکوپی و مغناطیسی آلیاژ سه تایی 2 Zr0.5Ti0.5Cr},
booktitle = {بیستمین همایش بلورشناسی و کانی شناسی ایران},
year = {2013},
location = {اهواز, ايران},
keywords = {Zr0.5Ti0.5Cr2 alloy; induction melting method; C14-type Laves phase},
}
%0 Conference Proceedings
%T ساخت و مشخصه یابی ساختاری، میکروسکوپی و مغناطیسی آلیاژ سه تایی 2 Zr0.5Ti0.5Cr
%A رضا سرحدی
%A عربی, هادی
%A فائز پورآرین
%J بیستمین همایش بلورشناسی و کانی شناسی ایران
%D 2013