یازدهمین کنفرانس ماده چگال انجمن فیزیک ایران , 2013-01-26

عنوان : ( سنتز و بررسی ساختار نانوذرات هسته پوسته FePt/Cu2O )

نویسندگان: حسین زینلی (دانشحو) , سید علی سبط , هادی عربی , حسین اکبری (دانشجو) ,
فایل: Full Text

استناددهی: BibTeX | EndNote

چکیده

Monodisperse FePt nanoparticles were successfully synthesized using the chemical polyol process. Annealing at the high temperatures is required to achieve the hard ferromagnetic behavior with L10 phase. Annealing causes the surfactant surrounding particles to be decomposed. Under such circumstances, FePt particles are agglomerated, and their size increases. In this research, for the first time, Cu2O oxide particle with a high melting point was used as the shell around FePt core particles to prevent agglomeration. As the result coercivity, Hc, of FePt and FePt/Cu2O nanoparticles after annealing at 750 oC were equal to 10 and 4.5 kOe, respectively

کلمات کلیدی

, FePt/Cu2O, Core-Shell, Nanoparticles, polyol process, FePt nanoparticles
برای دانلود از شناسه و رمز عبور پرتال پویا استفاده کنید.

@inproceedings{paperid:1037677,
author = {حسین زینلی (دانشحو) and سید علی سبط and عربی, هادی and حسین اکبری (دانشجو)},
title = {سنتز و بررسی ساختار نانوذرات هسته پوسته FePt/Cu2O},
booktitle = {یازدهمین کنفرانس ماده چگال انجمن فیزیک ایران},
year = {2013},
location = {شاهزود, ايران},
keywords = {FePt/Cu2O; Core-Shell; Nanoparticles; polyol process; FePt nanoparticles},
}

[Download]

%0 Conference Proceedings
%T سنتز و بررسی ساختار نانوذرات هسته پوسته FePt/Cu2O
%A حسین زینلی (دانشحو)
%A سید علی سبط
%A عربی, هادی
%A حسین اکبری (دانشجو)
%J یازدهمین کنفرانس ماده چگال انجمن فیزیک ایران
%D 2013

[Download]