n this study the effect of thermal spray process on wear resistance of NiAl/Cr2C3 thermal spray coating has been investigated. For this purpose the NiAl power mixed with 10 %wt. Cr2C3 powder and milled for 1 hrs at argon atmosphere. The APS parameters such as voltage (V), current (A), spray distance (mm), powder feed rate (gr/min), were optimize using a response surface methodology. For investigation effect of spray parameters on quality of coatings, the porosity and wear resistance of coatings analyzed with SEM and pin on disk wear test. Results show that increase of voltage and current are more effective other parameters. Increasing of powder feed rate and spray distance raised porosity of coatings