Nowadays, constructing hetero-structure materials is an efficacious procedure to uplift the electrochemical performance of layered double hydroxide (LDH) materials. The logical design of such elegant nanostructures is still challenging. Herein, NiCo-LDH nanosheets derived from Co-ZIF grown on graphene/polyaniline nanotube (G/PANI-NT)@cotton cloth (CC) was synthesized by a facile and novel two-step strategy for supercapacitors. Such hetero-structures give a 30.63 m2 g???? 1 surface area and more subjected electrochemical active sites. The supercapacitor performance results exhibit that the NiCo-LDH/G/PANI-NT@CC electrode has the best supercapacitor performance when it is used as a pseudocapacitor. By the ratio of Ni/Co = 2:1 in the precursor solution, the electrode shows an areal specific capacitance of 88.15 mF cm???? 2 at a current density of 0.075 mA cm???? 2. The electrochemical performance of the electrodes was perused using a redox-additive electrolyte. The electrochemical performance of the NiCo-LDH/G/PANI-NT@CC electrode was amended using K2S2O8 in a 3 M KOH solution. Considerably, the areal specific capacitance of NiCo-LDH/G/PANI-NT@CC (181.17 mF cm???? 2) increased to 431.30 mF cm???? 2, by changing the K2S2O8 concentration in KOH solution at a current density of 0.075 mA cm???? 2. Long-term stability test demonstrates that 84.05 % of the original capacitance remains after 10,000 cycles at the current density of 0.2 mA cm???? 2. The results indicate that NiCo-LDH/G/PANI-NT@CC will be an appropriate candidate for high-performance supercapacitors. The NiCo-LDH/G/PANI-NT@CC//NiCo-LDH/G/PANINT@ CC flexible solid-state supercapacitor was assembled with the PVA/KOH gel electrolyte.

Keywords