Title : ( Fatigue Anisotropy in a Wrought Aluminum Alloy )
Authors: Ahad Zabett , Alan Plumtree ,
Full TextAbstract
The influence of anisotropic microstructure on fatigue crack nucleation and short crack growth of a wrought aluminum alloy was studied at an intermediate stress amplitude. The longitudinal direction specimens had the shortest lives caused by early nucleation of cracks from particles. The transverse direction specimens possessed the longest lives since more grain boundaries hindered fatigue crack growth.
The influence of anisotropic microstructure on fatigue crack nucleation and short crack growth of a wrought aluminum alloy was studied at an intermediate stress amplitude. The longitudinal direction specimens had the shortest lives caused by early nucleation of cracks from particles. The transverse direction specimens possessed the longest lives since more grain boundaries hindered fatigue crack growth.
Keywords
, خستگی, انیزوتروپی, آلومینیوم T351-2024
@inproceedings{paperid:1006700,
author = {Zabett, Ahad and Alan Plumtree},
title = {Fatigue Anisotropy in a Wrought Aluminum Alloy},
booktitle = {The Fifth International Conference on Fatigue and Fatigue Thresholds},
year = {1993},
location = {Montreal},
keywords = {خستگی، انیزوتروپی، آلومینیوم T351-2024},
}
%0 Conference Proceedings
%T Fatigue Anisotropy in a Wrought Aluminum Alloy
%A Zabett, Ahad
%A Alan Plumtree
%J The Fifth International Conference on Fatigue and Fatigue Thresholds
%D 1993