Bis(indenyl)zirconium dichloride as a catalyst was synthesized using a modified method at the room temperature. Polymerization of ethylene and copolymerization of ethylene and propylene were carried out by this metallocene catalyst. Ethylene propylene (P/E) feed ratios of 0.25, 0.5, 1, and 2 were employed into the copolymerization systems. Copolymerization conditions like cocatalyst/catalyst ratio, copolymerization temperature, feed ratio and the viscosityaverage molecular weight (Mv) changing with copolymerization temperature were investigated. Higher ratio of [Al]/[Zr]=750:1 increased the activity of the catalyst. However, higher concentration of the cocatalyst slightly reduced the activity. Viscosity-average molecular weight of polymer decreased with high ratio of [Al]/[Zr]. The highest activity was obtained at 60oC. Increases in copolymerization temperature decreased the viscosity-average molecular weight and Et content of the polymeric products. Increases in propylene content of the feed ratio produced amorphous polymers with products of increased glass transition temperatures. Kinetic reaction displayed a decay type of reaction.

کلمات کلیدی