n this work, first multi-wall carbon nanotubes (MWCNTs) with outer diameter about 20–30 nm are synthesized by a CVD method; they have been purified and functionalized with a two-step process. The approach consists of thermal oxidation and subsequent chemical oxidation. Then, monosize FePt nanoparticles along carbon nanotubes surface are synthesized by a Polyol process. The synthesized FePt nanoparticles are about 2.5 nm in size and they have superparamagnetic behavior with fcc structure. The CNTs surfaces as a substrate prevent the coalescence of particles during thermal annealing. Annealing at the temperature higher than 600 ∘C for 2 h under a reducing atmosphere (90 % Ar + 10 % H2) leads to phase transition from fcc to fct-L10 structure. So, the magnetic behavior changes from the superparamagnetic to the ferromagnetic. Furthermore, after the phase transition, the FePt nanoparticles have finite size with an average of about 3.5 nm and the coercivity of particles reaches 5.1 kOe. Applied Physics A Applied Physics A Look Inside Share Share this content on Facebook Share this content on Twitter Share this content on LinkedIn Within this Article Introduction Experimental Results and discussion Conclusions References References Other actions Export citations Register for Journal Updates About This Journal Reprints and Permissions

Keywords