Title : ( Synthesis of pressure-sensitive adhesives based on butyl acrylate, effect of cross-linking agent )

Authors: hadi babaei , Gholamhossein Zohuri , M. Gholami , M. Shahidi ,

Citation: BibTeX | EndNote

Abstract

Synthesis of acrylate pressure sensitive adhesives (PSAs) latex is accomplished through out a semi-continuous emulsion copolymerization using butyl acrylate (BA) and acrylic acid monomers with urea formaldehyde resin (UF) as cross-linking agent to controlling the adhesive properties. Effect of prepared urea formaldehyde resin on the copolymer properties such as shear strength, tack and peel strength was investigated. As the amount of urea formaldehyde was increased (up to 2.20%) in the resin, shear strength was increased from 230 kPa to a limited value of about 513 kPa, peel strength was increased from 0.23 N/mm to 0.31 N/mm, however, the amount of tack of the latex was reduced (from 2.9 cm to 5.5 cm).

Keywords

, pressure sensitive adhesive, emulsion polymerization, cross-linking agent, adhesive, acrylate latex.
برای دانلود از شناسه و رمز عبور پرتال پویا استفاده کنید.

@inproceedings{paperid:1069464,
author = {Babaei, Hadi and Zohuri, Gholamhossein and M. Gholami and M. Shahidi},
title = {Synthesis of pressure-sensitive adhesives based on butyl acrylate, effect of cross-linking agent},
booktitle = {بیستمین کنگره شیمی ایران، دانشگاه فردوسی مشهد},
year = {2018},
location = {مشهد, IRAN},
keywords = {pressure sensitive adhesive; emulsion polymerization; cross-linking agent; adhesive; acrylate latex.},
}

[Download]

%0 Conference Proceedings
%T Synthesis of pressure-sensitive adhesives based on butyl acrylate, effect of cross-linking agent
%A Babaei, Hadi
%A Zohuri, Gholamhossein
%A M. Gholami
%A M. Shahidi
%J بیستمین کنگره شیمی ایران، دانشگاه فردوسی مشهد
%D 2018

[Download]